Aluminum Checkered Plate Five Bar for Truck Body 1060 3003 5052
Product Description
1000 series aluminum alloy represents 1050, 1060, 1100 series. Of
all the series, 1000 series belongs to the series with the highest
aluminium content. The purity can reach over 99.00%. Because it
does not contain other technical elements, the production process
is relatively simple and the price is relatively cheap. It is the
most commonly used series in conventional industries. The majority
of the market circulation is 1050 and 1060 series. The lowest
aluminium content of 1000 series aluminium sheets is determined by
the last two Arabic numerals. For example, the last two Arabic
numerals of 1050 series are 50. According to the naming principle
of international brands, the aluminium content must be above 99.5%
before qualified products are obtained. Our country's aluminium
alloy technical standard (gB/T3880-2006) also clearly stipulates
that the aluminium content of 1050 reaches 99.5%. Similarly, the
aluminium content of 1060 series aluminium plates must reach 99.6%
3000 series aluminium alloy represents 3003, 3A21 mainly. The
production process of 3000 series aluminium sheet in China is
excellent. 3000 series aluminium bar is mainly composed of
manganese. The content is between 1.0 and 1.5, which is a series
with better anti-rust function.
The 5000 series of aluminium alloys represent 5052, 5005, 5083 and
5A05 series. The 5000 series aluminium bar belongs to the more
commonly used alloy aluminium plate series, the main element is
magnesium, the content of magnesium is between 3-5%. It can also be
called Al-Mg alloy. Its main characteristics are low density, high
tensile strength, high elongation and good fatigue strength, but it
can not be strengthened by heat treatment. In the same area, the
weight of Al-Mg alloy is lower than that of other series. It is
also widely used in conventional industry. In our country, 5000
series aluminium sheet belongs to one of the more mature aluminium
sheet series.
| Aluminium Checker Sheet Specification |
| Alloy | 1050/1060/1100/3003/5052/5754/5083/6061/6063/6060/6082/8011 |
| Temper | H14,H18,H24,H32 ,H112, H114, T4,T6 ,T651,O |
| Thickness (mm) | 1.0 mm to 6 mm |
| Width (mm) | Up to 1800mm |
| Length (mm) | Up to 6000mm |
| Standard | GB/T14001-2004,ISO14001:2024, GB/T19001-2008,ISO9001:2008,SGS |
| MOQ | 5ton |
| Application | 1)Decorated inside and outside the car /building frame, windows,
doors, ceiling, decorating panel and curtain wall |
| 2)Household appliances: refrigerators, microwave ovens, audio
equipment, etc. |
| Delivery time | within 20-30 days after received the payment |
| Payment terms | L/C T/T |
Technical Property
| Alloy | Temper | Thickness(mm) | Tensile strength(Mpa) | Yeild strength(Mpa) | Elongation(%) |
| Min |
| 1060 | 0 | >0. 20 — 0, 30 | 60—100 | 15 | 15 |
| >0.30—0,50 | 18 |
| >0. 50-1. 50 | 23 |
| >1. 5-6.00 | 25 |
| >6. 00 — 80, 00 | 25 |
| H12 H22 | >0.50 —1,50 | 80 — 120 | 60 | 6 |
| >1. 50 — 6,00 | 12 |
| H14 H24 | >0. 30 — 0, 50 | 95-135 | 70 | 2 |
| >0.50 — 0. 80 | 2 |
| >0. 80—1. 50 | 4 |
| >1.50 — 3.00 | 6 |
| >3.00 — 6. 00 | 10 |
| H16 H26 | >0.20-0. 30 | 110 — 155 | 75 | 1 |
| >0. 30 — 0.50 | 2 |
| >0. 50 — 0. 80 | 2 |
| >0.80 〜1.50 | 3 |
| >1. 50 — 4. 00 | 5 |
| H18 | >0. 20 — 0.30 | 125 | 85 | 1 |
| >0. 30 — 0, 50 | 2 |
| >0.50 — 1.50 | 3 |
| >1,50-3.00 | 4 |
| H112 | >4. 50〜5. D0 | 75 | | 10 |
| >6. 00 — 12. 50 | 75 | 10 |
| >12*50 — 40.00 | 70 | —— |
| >40.00-80.00 : | 60 | |
| Alloy | Temper | Thickness(mm) | Tensile strength(Mpa) | Yeild strength(Mpa) | Elongation(%) |
| Min |
| 1O5OA | 0 | >0. 20—0.50 | 60-100 | | 15 |
| >0,50 — 1,50 | 20 |
| >0.8-1.5 | 20 | 25 |
| >1.5-6.0 | 28 |
| >6. 00—50, 00 | 30 |
| H12 | >0.20 — 0. 50 | 80-120 | | 2 |
| >0.50 — 1.50 | 65 | 4 |
| >1. 50 — 3.00 | 5 |
| >3.00 — 6.00 | 7 |
| H22 | >0. 20 — 0. 50 | 80 | | 4 |
| >0. 50—1. 50 | 65 | 5 |
| >1. 50 — 3. 00 | 6 |
| >3. 00 — 6. 00 | 11 |
| H14 | >0. 20 — 0.50 | 95-130 | | 2 |
| >0. 50 — 1. 50 | 75 | 3 |
| >1.50 — 3.00 | 4 |
| >3.00 — 6. 00 | 5 |
| H24 | >0. 20—G. 50 | 95 | | 3 |
| >0. 50—1.50 | 75 | 4 |
| >1.50 — 3.00 | 5 |
| >3.00—6. 00 | 8 |
| H16 | >0.20 — 0. 50 | 120-150 | 85 | 1 |
| >0, 50 — 1.50 | 2 |
| >1. 50 — 4. 00 | 3 |
| H26 | >0.20 — 0. 50 | 120 | | 2 |
| >0, 50 — 1.50 | | 3 |
| >1. 50 — 4. 00 | 85 | 4 |
| H18 | >0. 20—0.50 | 130 | | 1 |
| >0. 50 — 1. 50 | 2 |
| >1. 50 — 3. 00 | 3 |
| H112 | >4. 50— 12. 50 | 85 | 45 | 10 |
| >12,50—75,00 | 80 | 45 | 10 |
|
| Alloy | Temper | Thickness(mm) | Tensile strength(Mpa) | Yeild strength(Mpa) | Elongation(%) |
| Min |
| 3003 | O H111 | >0. 20—0. 50 | 95-135 | 35 | 15 |
| >0. 50 — 1. 50 | 17 |
| >1. 50 — 3. 00 | 20 |
| >3.00 — 6. 00 | 23 |
| >6.0-12.5 | 24 |
| >12.5-50 | |
| H12 | >0. 20—0. 50 | 120-160 | 90 | 3 |
| >0. 50 — 1. 50 | 4 |
| >1.50 — 3.00 | 5 |
| >3. 00 — 6. 00 | 6 |
| H14 | >0. 20 — 0. 50 | 145-195 | 125 | 2 |
| >0. 5- 50 | 2 |
| >1. 50 — 3. 00 | 3 |
| >3. 00—6.0 | 4 |
| H16 | >0. 20 — 0. 50 | 170-210 | 140 | 2 |
| >0.50 — 1.50 | 3 |
| >1. 50—4. 00 | 3 |
| H18 | >0. 20 — 0. 50 | 190 | 170 | 1 |
| >0. 50—1. 50 | 2 |
| >1. 50 — 3. 00 | 2 |
| H22 | >0. 20—0. 50 | 120-160 | 80 | 6 |
| >0. 50 — 1.50 | 7 |
| >1.50 — 3.00 | 8 |
| >3. 0—6.0 | 9 |
| H24 | >0. 20—0. 50 | 145-195 | 115 | 4 |
| >0. 50 — 1.50 | 4 |
| >1.50 —3. 00 | 5 |
| H26 | >0. 20 — 0. 50 | 170-210 | 140 | 2 |
| >0.50—1.50 | 3 |
| >1.50 — 3. 00 | 3 |
| H28 | >0,20 — 0,50 | 190 | 160 | 2 |
| >0. 50〜L 50 | 2 |
| >1. 50—3. 00 | 3 |
| Alloy | Temper | Thickness(mm) | Tensile strength(Mpa) | Yeild strength(Mpa) | Elongation(%) |
| Min |
| 5052 | H111 O | >0. 20 — 0. 50 | 170 — 215 | 65 | 12 |
| >0. 50 — 1. 50 | 14 |
| >1.55 — 3.00 | 16 |
| >3. 00 — 6. 00 | 18 |
| >6.00 — 12. 50 | 165-215 | 19 |
| >12. 50 — 50.00 | — |
| H12 | >0. 20 — 0. 50 | 210 — 260 | 160 | 4 |
| >0.5-1.5 | 5 |
| >1.50 —3.00 | 6 |
| >3, 00 — 6. 00 | 8 |
| H14 | >0. 20 — 0. 50 | 230-280 | 180 | 3 |
| >0.50-1.50 | 3 |
| >1. 50 -3. 00 | 4 |
| >3.00 — 6.00 | 4 |
| H16 | >0. 20 — 0, 50 | 250—300 | 210 | 2 |
| >0. 50 — 1. 50 | 3 |
| >1. 5- 3.0 | 3 |
| >3.00 — 4. 00 | 3 |
| H18 | >0. 20-0.50 | 270 | 240 | 1 |
| >0. 50 — 1. 50 | 2 |
| > 1.50 — 3.00 | 2 |
| H22 H32 | >0. 20—0. 50 | 210 — 260 | 130 | 5 |
| >0. 50-1.50 | 6 |
| >1.50 — 3.00 | 7 |
| >3. 00 — 6. 00 | 10 |
| H24 H34 | >0. 20 — 0. 50 | 230 — 280 | 150 | 4 |
| >0.50 — 1. 50 | 5 |
| >1,50 — 3.00 | 6 |
| >3.00 — 6.00 | 7 |
| H26 H36 | >0. 20 — 0.50 | 250 — 300 | 180 | 3 |
| >0. 50 — 1, 50 | 4 |
| >1.50—3.00 | 5 |
| >3. 00—4. 00 | 6 |
| H38 H28 | >0. 20 — 0, 50 | 270 | 210 | 3 |
| >0. 50~1. 5 | 3 |
| >1. 50 — 3. 00 | 4 |
| H112 | >6.00—12. 50 | 190 | 80 | 7 |
| >12. 50 — 40,00 | 170 | 70 | |
| >40, 00 — 80, 00 | 170 | 70 | |
Aluminum Checker Sheet Advantages
1. Accurate size, good anti-slip effect,wide range of applications
2. Strong plasticity, easy forming and excellent processing
performance.
3. Embossed aluminum sheet can form a dense and strong oxide film
on aluminum surface to prevent the intrusion of oxygen, so it has
good corrosion resistance.
4. Good elongation and tensile strength, fully able to meet the
normal processing requirements (stamping, stretching), high
formability
5. The surface quality of aluminum checker plate is good, no oil
spots, waves, scratches, roller marks, neat trimming, no burrs.
Company Introduction
Chongqing Dongchong AluminumCo,.Ltd. is a manufacturer of Aluminium
products with well-equipped,experienced work team.Our company is
equipped with international advanced aluminum production lines. We
also own press machine, double-sided milling, cutting machine,
recoiler, grinding machine, quenching furnace, tension
pre-stretching machine, annealing furnace, smelting furnace machine
and so on. We mainly provide aluminum and its alloy sheets, plates,
strips, circles, foils, embossed coils, colorful painted aluminum
coils, sheet products, etc.With a wide range, good quality,
reasonable prices and stylish designs, our products can meet most
of all customer needs.Our company established in 2002 and have been
in aluminium indurstry for more than 15 years.We have our own brand
and customized services are available too.We are an ISO9001:2008
certified company and our QC staff members have ten years'
experience in this area. To maintain a strict QC system, we not
only utilize precision testing instruments but also continuously
train our QA personnel regarding the latest testing principles.We
have established long term business relationships with customers in
many countries and areas in the world, including the USA, Canada,
Brazil, India, Chile, Nigeria, Ghana, Italy, etc. We will continue
providing high quality products and better services for our
customers, and welcome you to visit our company and establish good
business relationships with us.